Surface Coats

Makobond SC 576 is a high temperature black surface coat designed for composite parts and tooling. The SC 576 has minimal thermal expansion and with its thixotropic nature, makes it easy to apply to difficult areas. SC 576 has a resistance to chipping and cracking. SC 576 is like our SC 575 system; however, the SC 576 provides a longer pot life as well as a higher glass transition temperature.

Makobond SC 566 is a high temperature black surface coat. SC 566 is like our SC 565 system; however, the SC 566 provides a longer pot life as well as a higher glass transition temperature. SC 565 is designed for high temperature, tough applications. The hard surface created by SC 566 is resistant to scratches and cuts.

Makobond SC 565 is a very tough, high temperature black surface coat. The SC 565 is durable and resistant to scratches and cuttings. This is due to the very hard surface that is formed once the system is cured. SC 565 creates a hard surface with excellent heat resistance for long lasting parts.

Makobond Surface Coat 540 is a specialized epoxy infused with black graphite, ideal for tooling applications requiring moderate heat exposure. Its thin, paintable nature adheres well to contoured surfaces without dripping, thanks to its thin yet thixotropic viscosity. SC 540 is versatile, used in fabricating parts and structures, with excellent heat resistance for paint bake ovens and extreme temperatures.

Makobond SC 501 is an all-purpose, white surface coat. SC 501 is designed to be used for room temperature applications. The SC 501 system is thixotropic by nature making it easy to work with, without sagging or drag. SC 501 is resistant to chipping and can easy be sanded within 12 hours of application.

Makobond SC 504 is thixotropic surface coat system designed for tough applications. The mixed system is a smooth, creamy mix making it easy to mix and apply to difficult areas. SC 504 is tough and will stand up to difficult environments for a long time. The SC 504 is available in either black or white.